904L Stainless Steel Coil
Huien Metal
Product Details
Product name: Huien Metal 904L stainless steel coil
904L stainless steel strip, surface: 2B smooth surface, No.1 industrial surface, BA (6k) mirror, 8K mirror, drawing surface, frosted surface hardness (soft material, hard material) : deep drawing soft material; Hard material 1/4H, 1/2H, 3/4 h, H, EH, SH; HV 30-650 degrees.
It has high chromium content and sufficient nickel content. The addition of copper makes it have strong acid resistance, especially high resistance to chloride gap corrosion and stress corrosion cracking. It is not easy to appear corrosion spots and cracks, and its pitting resistance is slightly better than other steel, with good machinability and weldability. Non-magnetic in solid solution state;
The chemical composition of 904L is % C≤0.03, Si≤1.00, Mn≤2.00, P≤0.035, S≤0.03, Ni:23.0-25.0, Cr:18.0-20.0, Mo:3.0-4.0, Cu:4.0-5.0. Minimum mechanical properties of 904L alloy at room temperature: alloy and state :926, tensile strength (Rm N/mm2):490, yield strength (RP0.2N/mm2):216, elongation A5% :35.
904L (N08904, 14539) super austenitic stainless steel contains 14.0-18.0% chromium, 24.0-26.0% nickel, 4.5% molybdenum. 904L super austenitic stainless steel is a low-carbon, high-nickel, molybdenum austenitic stainless acid-resistant steel, which is a proprietary material imported from French H·S company. It has very good activation-passivation transition ability, excellent corrosion resistance, good corrosion resistance in non-oxidizing acids such as sulfuric acid, acetic acid, formic acid, phosphoric acid, and good corrosion resistance in neutral chloride ion-containing media Excellent pitting corrosion resistance, good crevice corrosion resistance and stress corrosion resistance. It is suitable for various concentrations of sulfuric acid below 70°C, and it is also resistant to acetic acid of any concentration and temperature under normal pressure, and has good corrosion resistance in the mixed acid of formic acid and acetic acid.
904L stainless steel material is a super austenitic stainless steel material, is a very low carbon content of high alloying austenitic stainless steel, has good corrosion resistance in dilute acids, designed for harsh corrosion conditions in the environment.
Chemical Composition And Mechanical Properties Of Stainless Steel Coils:
Grade | Chemical Composition (%) | Mechanieal Performece | |||||||
C | Si | Mn | P | S | Ni | Cr | Mo | Hardness | |
201 | ≤0.15 | ≤1.00 | 5.5/7.5 | ≤0.060 | ≤0.030 | 3.5/5.5 | 16.0/18.0 | HB≤241,HRB≤100, HV≤240 | |
304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.0/11.0 | 18.00/20.00 | HB≤187,HRB≤90,HV≤200 | |
316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187, HRB≤90 HV≤200 |
316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187, HRB≤90 HV≤200 |
410 | ≤0.15 | ≤1.00 | ≤1.25 | ≤0.060 | ≤0.03 | ≤0.060 | 11.5/13.5 | HB≤183, HRB≤88 HV≤200 | |
430 | ≤0.12 | ≤1.00 | ≤1.25 | ≤0.040 | ≤0.03 | 16.00/18.00 | HB≤183, HRB≤88 HV≤200 |
Product Details
Product name: Huien Metal 904L stainless steel coil
904L stainless steel strip, surface: 2B smooth surface, No.1 industrial surface, BA (6k) mirror, 8K mirror, drawing surface, frosted surface hardness (soft material, hard material) : deep drawing soft material; Hard material 1/4H, 1/2H, 3/4 h, H, EH, SH; HV 30-650 degrees.
It has high chromium content and sufficient nickel content. The addition of copper makes it have strong acid resistance, especially high resistance to chloride gap corrosion and stress corrosion cracking. It is not easy to appear corrosion spots and cracks, and its pitting resistance is slightly better than other steel, with good machinability and weldability. Non-magnetic in solid solution state;
The chemical composition of 904L is % C≤0.03, Si≤1.00, Mn≤2.00, P≤0.035, S≤0.03, Ni:23.0-25.0, Cr:18.0-20.0, Mo:3.0-4.0, Cu:4.0-5.0. Minimum mechanical properties of 904L alloy at room temperature: alloy and state :926, tensile strength (Rm N/mm2):490, yield strength (RP0.2N/mm2):216, elongation A5% :35.
904L (N08904, 14539) super austenitic stainless steel contains 14.0-18.0% chromium, 24.0-26.0% nickel, 4.5% molybdenum. 904L super austenitic stainless steel is a low-carbon, high-nickel, molybdenum austenitic stainless acid-resistant steel, which is a proprietary material imported from French H·S company. It has very good activation-passivation transition ability, excellent corrosion resistance, good corrosion resistance in non-oxidizing acids such as sulfuric acid, acetic acid, formic acid, phosphoric acid, and good corrosion resistance in neutral chloride ion-containing media Excellent pitting corrosion resistance, good crevice corrosion resistance and stress corrosion resistance. It is suitable for various concentrations of sulfuric acid below 70°C, and it is also resistant to acetic acid of any concentration and temperature under normal pressure, and has good corrosion resistance in the mixed acid of formic acid and acetic acid.
904L stainless steel material is a super austenitic stainless steel material, is a very low carbon content of high alloying austenitic stainless steel, has good corrosion resistance in dilute acids, designed for harsh corrosion conditions in the environment.
Chemical Composition And Mechanical Properties Of Stainless Steel Coils:
Grade | Chemical Composition (%) | Mechanieal Performece | |||||||
C | Si | Mn | P | S | Ni | Cr | Mo | Hardness | |
201 | ≤0.15 | ≤1.00 | 5.5/7.5 | ≤0.060 | ≤0.030 | 3.5/5.5 | 16.0/18.0 | HB≤241,HRB≤100, HV≤240 | |
304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.0/11.0 | 18.00/20.00 | HB≤187,HRB≤90,HV≤200 | |
316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187, HRB≤90 HV≤200 |
316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187, HRB≤90 HV≤200 |
410 | ≤0.15 | ≤1.00 | ≤1.25 | ≤0.060 | ≤0.03 | ≤0.060 | 11.5/13.5 | HB≤183, HRB≤88 HV≤200 | |
430 | ≤0.12 | ≤1.00 | ≤1.25 | ≤0.040 | ≤0.03 | 16.00/18.00 | HB≤183, HRB≤88 HV≤200 |
904L stainless steel roll implementation standard:
ASTM A240/ASME SA-240, ASTM A276, ASTM A182/ASME SA-182, ASTM A312/ASMES A312, ASTM B625/ASME B625, ASTM B673/ASME B673 904L, Al-904L, UNS N08904, SUS890L, F904L, W.-Nr. 1.4539, NAS 255, 00Cr20Ni25Mo4.5Cu
904L Quality Inspection
To test the surface quality of 904L stainless steel plate, usually wait until the pickling process after heat treatment. The pickling process can improve the finish and uniformity of 904L stainless steel plate surface. If the surface is not cleaned before heat treatment, the quality is not up to the standard, after pickling can not reach the standard. Therefore, in order to improve the quality of 904L stainless steel plate surface, before or during heat treatment, surface cleaning should be carried out.
904L stainless steel roll implementation standard:
ASTM A240/ASME SA-240, ASTM A276, ASTM A182/ASME SA-182, ASTM A312/ASMES A312, ASTM B625/ASME B625, ASTM B673/ASME B673 904L, Al-904L, UNS N08904, SUS890L, F904L, W.-Nr. 1.4539, NAS 255, 00Cr20Ni25Mo4.5Cu
904L Quality Inspection
To test the surface quality of 904L stainless steel plate, usually wait until the pickling process after heat treatment. The pickling process can improve the finish and uniformity of 904L stainless steel plate surface. If the surface is not cleaned before heat treatment, the quality is not up to the standard, after pickling can not reach the standard. Therefore, in order to improve the quality of 904L stainless steel plate surface, before or during heat treatment, surface cleaning should be carried out.