Chemical Composition: Carbon C: ≤0.08, Silicon Si: ≤1.00, Manganese Mn: ≤2.00, Sulfur S: ≤0.030, P: ≤0.035, Chromium Cr: 24.00 ~ 26.00, Nickel Ni: 19.00 ~ 22.00
310 Stainless Steel Bar
Huien Metal
310 Stainless Steel Bar
High temperature resistance, generally used in the boiler, automobile exhaust pipe.
Product name :310 stainless steel rod, 310S stainless steel rod
Diameter: 1.0MM above
Material :304, 304L, 321, 316, 316L, 310S, 630, 1Cr13, 2Cr13, 3Cr13, 1Cr17Ni2, duplex steel, antibacterial steel and other materials!
Application: petroleum, electronics, chemical, pharmaceutical, textile, food, machinery, construction, nuclear power, aerospace, military and other industries!
The 310 is a free cutting stainless steel containing sulfur and selenium respectively, for use in applications where the main requirement is free cutting and high surface finish. 303 stainless steel improves machinability and high temperature bonding resistance. Most suitable for automatic lathe. Bolts and nuts.
310 stainless steel is Austenitic type easy cutting rust resistant wear-resisting acid steel, in order to improve the performance of the steel, can be added in the steel no more than 0.60% molybdenum, corrosion resistance, good product machinability and fire resistance. 310 Mechanical properties of stainless steel after annealing stress removal, tensile strength 515MPa, yield 205MPa, elongation 40%. Stainless Steel 310 standard hardness HRB 90-100, HRC 20-25, Note: HRB100 = HRC20
Product Details
Product Name | 310 Stainless Steel Bar |
Thickness | 0.12-5mm, Customize |
Diameter | Round Bar: 0.1~500mm |
Size | Square Bar: 1mm*1mm~800mm*800mm |
Surface | Black, peeled, polishing, bright, sand blast, hair line, etc. |
Standard | ASTM A479,ASTM A276,ASTM A484, ASTM A582, ASME SA276, ASME SA484, GB/T1220, GB4226, etc. |
Quality Test | Support third party inspection and factory inspection |
Common Material | 201, 304、304L、TP304、TP316L、316、316L、316Ti、321、347H、310S, 409,410, 420, 430, 904L, 2205, 2507 |
Material | DX51D,DX52D,DX53D,DC51D,DC52D,DC53D,SGCC,SGCD,SGCE, Q195/Q235/Q345/Q390/Q420/Q460/Q500/S235jr/S235jo |
Technique | Hot rolled / Cold rolled |
Application | Construction, Ship building, Machinery manufacturing, Steel structure etc |
Tolerance | Thickness: ±0.01 mm Width: ±2 mm |
Grade | Chemical Composition (%) | Mechanieal Performece | |||||||
C | Si | Mn | P | S | Ni | Cr | Mo | Hardness | |
201 | ≤0.15 | ≤1.00 | 5.5/7.5 | ≤0.060 | ≤0.030 | 3.5/5.5 | 16.0/18.0 | HB≤241,HRB≤100, HV≤240 | |
304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.0/11.0 | 18.00/20.00 | HB≤187,HRB≤90,HV≤200 | |
316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187, HRB≤90 HV≤200 |
316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187, HRB≤90 HV≤200 |
410 | ≤0.15 | ≤1.00 | ≤1.25 | ≤0.060 | ≤0.03 | ≤0.060 | 11.5/13.5 | HB≤183, HRB≤88 HV≤200 | |
430 | ≤0.12 | ≤1.00 | ≤1.25 | ≤0.040 | ≤0.03 | 16.00/18.00 | HB≤183, HRB≤88 HV≤200 | ||
310 Stainless Steel Bar
High temperature resistance, generally used in the boiler, automobile exhaust pipe.
Product name :310 stainless steel rod, 310S stainless steel rod
Diameter: 1.0MM above
Material :304, 304L, 321, 316, 316L, 310S, 630, 1Cr13, 2Cr13, 3Cr13, 1Cr17Ni2, duplex steel, antibacterial steel and other materials!
Application: petroleum, electronics, chemical, pharmaceutical, textile, food, machinery, construction, nuclear power, aerospace, military and other industries!
The 310 is a free cutting stainless steel containing sulfur and selenium respectively, for use in applications where the main requirement is free cutting and high surface finish. 303 stainless steel improves machinability and high temperature bonding resistance. Most suitable for automatic lathe. Bolts and nuts.
310 stainless steel is Austenitic type easy cutting rust resistant wear-resisting acid steel, in order to improve the performance of the steel, can be added in the steel no more than 0.60% molybdenum, corrosion resistance, good product machinability and fire resistance. 310 Mechanical properties of stainless steel after annealing stress removal, tensile strength 515MPa, yield 205MPa, elongation 40%. Stainless Steel 310 standard hardness HRB 90-100, HRC 20-25, Note: HRB100 = HRC20
Product Details
Product Name | 310 Stainless Steel Bar |
Thickness | 0.12-5mm, Customize |
Diameter | Round Bar: 0.1~500mm |
Size | Square Bar: 1mm*1mm~800mm*800mm |
Surface | Black, peeled, polishing, bright, sand blast, hair line, etc. |
Standard | ASTM A479,ASTM A276,ASTM A484, ASTM A582, ASME SA276, ASME SA484, GB/T1220, GB4226, etc. |
Quality Test | Support third party inspection and factory inspection |
Common Material | 201, 304、304L、TP304、TP316L、316、316L、316Ti、321、347H、310S, 409,410, 420, 430, 904L, 2205, 2507 |
Material | DX51D,DX52D,DX53D,DC51D,DC52D,DC53D,SGCC,SGCD,SGCE, Q195/Q235/Q345/Q390/Q420/Q460/Q500/S235jr/S235jo |
Technique | Hot rolled / Cold rolled |
Application | Construction, Ship building, Machinery manufacturing, Steel structure etc |
Tolerance | Thickness: ±0.01 mm Width: ±2 mm |
Grade | Chemical Composition (%) | Mechanieal Performece | |||||||
C | Si | Mn | P | S | Ni | Cr | Mo | Hardness | |
201 | ≤0.15 | ≤1.00 | 5.5/7.5 | ≤0.060 | ≤0.030 | 3.5/5.5 | 16.0/18.0 | HB≤241,HRB≤100, HV≤240 | |
304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.0/11.0 | 18.00/20.00 | HB≤187,HRB≤90,HV≤200 | |
316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187, HRB≤90 HV≤200 |
316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187, HRB≤90 HV≤200 |
410 | ≤0.15 | ≤1.00 | ≤1.25 | ≤0.060 | ≤0.03 | ≤0.060 | 11.5/13.5 | HB≤183, HRB≤88 HV≤200 | |
430 | ≤0.12 | ≤1.00 | ≤1.25 | ≤0.040 | ≤0.03 | 16.00/18.00 | HB≤183, HRB≤88 HV≤200 | ||